ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe
  • ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe
  • ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe
  • ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe
  • ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe
ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe

ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe

Place of Origin China
Brand Name TISCO BAOSTEEL
Certification SGS BV
Model Number Carbon Steel Sheet
Product Details
Name:
ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe
Length:
1000-12000mm,As Customers' Requirement
Thickness:
0.5-100mm,6-400mm,1mm-120mm,0.15mm-300mm
Width:
600-2500mm,600mm-1250mm,1.8m,305mm/355mm/455mm/510mm
Surface:
Galvanized Coated,Black Painted,PE Coated,Black Painting Or Galvanized,etc.
Material:
A36 A283 A387 1008 4320 SS400 S235jr
High Light: 

Oil Steel Spiral Welded Tube Pipe

,

Large Diameter Seamless Carbon Pipes

,

SSAW steel pipe

Payment & Shipping Terms
Minimum Order Quantity
1 ton
Price
To be negotiated
Packaging Details
Kraft paper, wooden case, packaging according to customer requirements
Delivery Time
10-15 days after advance payment
Payment Terms
L/C, T/T
Supply Ability
8,000 ton per month
Product Description

ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe

 

 

ANSI / API 5L specifies the manufacture of two product levels (PSL1 and PSL2) of seamless and welded steel pipe for the use of a pipeline in the transportation of petroleum and natural gas. For material use in a sour service application, refer to Annex H; for offshore service application, refer to Annex J of API 5L 45th Edition.

 

Ingots, blooms, billets, coils or plates used for the manufacture of pipe shall be made via basic oxygen, electric furnace or open hearth in combination with a ladle refining process. For PSL2, the steel shall be killed and melted according to a fine grain practice. Coil or plate used for PSL2 pipe shall not contain any repair welds.

Delivery condition

PSL Delivery Condition Pipe grade
PSL1 As-rolled, normalized, normalizing formed A
  As-rolled, normalizing rolled, thermomechanical rolled, thermo-mechanical formed, normalizing formed, normalized, normalized and tempered or if agreed Q&T SMLS only B
  As-rolled, normalizing rolled, thermomechanical rolled, thermo-mechanical formed, normalizing formed, normalized, normalized and tempered X42, X46, X52, X56, X60, X65, X70
PSL 2 As-rolled BR, X42R
  Normalizing rolled, normalizing formed, normalized or normalized and tempered BN, X42N, X46N, X52N, X56N, X60N
  Quenched and tempered BQ, X42Q, X46Q, X56Q, X60Q, X65Q, X70Q, X80Q, X90Q, X100Q
  Thermomechanical rolled or thermomechanical formed BM, X42M, X46M, X56M, X60M, X65M, X70M, X80M
  Thermomechanical rolled X90M, X100M, X120M
  The suffice (R, N, Q or M) for PSL2 grades, belongs to the steel grade  

 

 

Chemical Composition for PSL 1 pipe with t ≤ 0.984”

 

Steel Grade Mass fraction, % based on heat and product analyses a,g
C Mn P S V Nb Ti
max b max b max max max max max
Seamless Pipe
A 0.22 0.9 0.3 0.3 – – –
B 0.28 1.2 0.3 0.3 c,d c,d d
X42 0.28 1.3 0.3 0.3 d d d
X46 0.28 1.4 0.3 0.3 d d d
X52 0.28 1.4 0.3 0.3 d d d
X56 0.28 1.4 0.3 0.3 d d d
X60 0.28 e 1.40 e 0.3 0.3 f f f
X65 0.28 e 1.40 e 0.3 0.3 f f f
X70 0.28 e 1.40 e 0.3 0.3 f f f
Welded Pipe
A 0.22 0.9 0.3 0.3 – – –
B 0.26 1.2 0.3 0.3 c,d c,d d
X42 0.26 1.3 0.3 0.3 d d d
X46 0.26 1.4 0.3 0.3 d d d
X52 0.26 1.4 0.3 0.3 d d d
X56 0.26 1.4 0.3 0.3 d d d
X60 0.26 e 1.40 e 0.3 0.3 f f f
X65 0.26 e 1.45 e 0.3 0.3 f f f
X70 0.26e 1.65 e 0.3 0.3 f f f
a. Cu ≤ = 0.50% Ni; ≤ 0.50%; Cr ≤ 0.50%; and Mo ≤ 0.15%,
b. For each reduction of 0.01% below the specified maximum concentration for carbon, an increase of 0.05% above the specified maximum concentration for Mn is permissible, up to a maximum of 1.65% for grades ≥ L245 or B, but ≤ L360 or X52; up to a maximum of 1.75% for grades > L360 or X52, but < L485 or X70; and up to a maximum of 2.00% for grade L485 or X70.,
c. Unless otherwise agreed NB + V ≤ 0.06%,
d. Nb + V + TI ≤ 0.15%,
e. Unless otherwise agreed.,
f. Unless otherwise agreed, NB + V = Ti ≤ 0.15%,
g. No deliberate addition of B is permitted and the residual B ≤ 0.001%

 

 

Chemical Composition for PSL 2 pipe with t ≤ 0.984”

 

Steel Grade Mass fraction, % based on heat and product analyses Carbon Equiv a
C Si Mn P S V Nb Ti Other CE IIW CE Pcm
max b max max b max max max max max max max
Seamless and Welded Pipe
BR 0.24 0.4 1.2 0.025 0.015 c c 0.04 e,l 0.43 0.25
X42R 0.24 0.4 1.2 0.025 0.015 0.06 0.05 0.04 e,l 0.43 0.25
BN 0.24 0.4 1.2 0.025 0.015 c c 0.04 e,l 0.43 0.25
X42N 0.24 0.4 1.2 0.025 0.015 0.06 0.05 0.04 e,l 0.43 0.25
X46N 0.24 0.4 1.4 0.025 0.015 0.07 0.05 0.04 d,e,l 0.43 0.25
X52N 0.24 0.45 1.4 0.025 0.015 0.1 0.05 0.04 d,e,l 0.43 0.25
X56N 0.24 0.45 1.4 0.025 0.015 0.10f 0.05 0.04 d,e,l 0.43 0.25
X60N 0.24f 0.45f 1.40f 0.025 0.015 0.10f 0.05f 0.04f g,h,l As agreed
BQ 0.18 0.45 1.4 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
X42Q 0.18 0.45 1.4 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
X46Q 0.18 0.45 1.4 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
X52Q 0.18 0.45 1.5 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
X56Q 0.18 0.45f 1.5 0.025 0.015 0.07 0.05 0.04 e,l 0.43 0.25
X60Q 0.18f 0.45f 1.70f 0.025 0.015 g g g h,l 0.43 0.25
X65Q 0.18f 0.45f 1.70f 0.025 0.015 g g g h,l 0.43 0.25
X70Q 0.18f 0.45f 1.80f 0.025 0.015 g g g h,l 0.43 0.25
X80Q 0.18f 0.45f 1.90f 0.025 0.015 g g g i,j As agreed
X90Q 0.16f 0.45f 1.9 0.02 0.01 g g g j,k As agreed
X100Q 0.16f 0.45f 1.9 0.02 0.01 g g g j,k As agreed
Welded Pipe
BM 0.22 0.45 1.2 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
X42M 0.22 0.45 1.3 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
X46M 0.22 0.45 1.3 0.025 0.015 0.05 0.05 0.04 e,l 0.43 0.25
X52M 0.22 0.45 1.4 0.025 0.015 d d d e,l 0.43 0.25
X56M 0.22 0.45f 1.4 0.025 0.015 d d d e,l 0.43 0.25
X60M 0.12f 0.45f 1.60f 0.025 0.015 g g g h,l 0.43 0.25
X65M 0.12f 0.45f 1.60f 0.025 0.015 g g g h,l 0.43 0.25
X70M 0.12f 0.45f 1.70f 0.025 0.015 g g g h,l 0.43 0.25
X80M 0.12f 0.45f 1.85f 0.025 0.015 g g g i,j .043f 0.25
X90M 0.1 0.55f 2.10f 0.02 0.01 g g g i,j – 0.25
X100M 0.1 0.55f 2.10f 0.02 0.01 g g g i,j – 0.25
a. SMLS t>0.787”, CE limits shall be as agreed. The CEIIW limits applied fi C > 0.12% and the CEPcm limits apply if C ≤ 0.12%,
b. For each reduction of 0.01% below the specified maximum for C, an increase of 0.05% above the specified maximum for Mn is permissible, up to a maximum of 1.65% for grades ≥ L245 or B, but ≤ L360 or X52; up to a maximum of 1.75% for grades > L360 or X52, but < L485 or X70; up to a maximum of 2.00% for grades ≥ L485 or X70, but ≤ L555 or X80; and up to a maximum of 2.20% for grades > L555 or X80.,
c. Unless otherwise agreed Nb = V ≤ 0.06%,
d. Nb = V = Ti ≤ 0.15%,
e. Unless otherwise agreed, Cu ≤ 0.50%; Ni ≤ 0.30% Cr ≤ 0.30% and Mo ≤ 0.15%,
f. Unless otherwise agreed,
g. Unless otherwise agreed, Nb + V + Ti ≤ 0.15%,
h. Unless otherwise agreed, Cu ≤ 0.50% Ni ≤ 0.50% Cr ≤ 0.50% and MO ≤ 0.50%,
i. Unless otherwise agreed, Cu ≤ 0.50% Ni ≤ 1.00% Cr ≤ 0.50% and MO ≤ 0.50%,
j. B ≤ 0.004%,
k. Unless otherwise agreed, Cu ≤ 0.50% Ni ≤ 1.00% Cr ≤ 0.55% and MO ≤ 0.80%,
l. For all PSL 2 pipe grades except those grades with footnotes j noted, the following applies. Unless otherwise agreed no intentional addition of B is permitted and residual B ≤ 0.001%.

 

Mechanical properties

 

Pipe Grade Tensile Properties – Pipe Body of SMLS and Welded Pipes PSL 1 Seam of Welded Pipe
Yield Strength a Tensile Strength a Elongation Tensile Strength b
Rt0,5 PSI Min Rm PSI Min (in 2in Af % min) Rm PSI Min
A 30,500 48,600 c 48,600
B 35,500 60,200 c 60,200
X42 42,100 60,200 c 60,200
X46 46,400 63,100 c 63,100
X52 52,200 66,700 c 66,700
X56 56,600 71,100 c 71,100
X60 60,200 75,400 c 75,400
X65 65,300 77,500 c 77,500
X70 70,300 82,700 c 82,700

 

 

Hydrostatic test

 

Pipe to withstand a hydrostatic test without leakage through the weld seam or the pipe body. Jointers need not be hydrostatic tested provide the pipe sections used were successfully tested.

Bend test

 

No cracks shall occur in any portion of the test piece and no opening of the weld shall occur.

Flattening test

 

Acceptance criteria for flattening test shall be:

  • EW pipes D<12.750 in:
  • X60 with T 500in. There shall be no opening of the weld before the distance between the plates is less than 66% of the original outside diameter. For all grades and wall, 50%.
  • For pipe with a D/t > 10, there shall be no opening of the weld before the distance between the plates is less than 30% of the original outside diameter.
  • For other sizes refer to the full API 5L specification.

 

 

ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe 0

 

ASTM A36 SSAW Seamless Steel Pipe Large Diameter Oil Steel Spiral Welded Tube Pipe 1 

Payment Terms

1.Payment: T/T, L/C, Western Union, MoneyGram,PayPal; 30% deposits; 70% balance before delivery.

2.MOQ: 1pcs

3.Warranty : 3 years

4.Package Informations: 1) EXPORT, In 20 feet (GW 25 ton) or 40 feet Container (GW 25 ton)

2)as customer's requirement

 

Why choose us?

(1) The leading exporter in China special steel industry.

(2) Large stocks for various sizes, fast delivery date.

(3) Good business relationship with China famous factories.

(4) More than 7 years steel exporting experience.

(5) Good after-sales service guarantee.

Tags:

black steel seamless pipe astm a106,

0.8mm black steel seamless pipe,

8 inch astm a106 seamless pipe

Recommended Products

Contact Us at Any Time

+86 18762819931
G16, 66 Chunhui Middle Road, Xishan Economic Development Zone, Wuxi city, China
8618762819931
sales03@laiyuan-steels.com
Send your inquiry directly to us