SGS 0.1mm Thickness Copper Flat Sheets C26800 Thin Copper Sheets For Crafts
Copper Alloys C26800 is used for electrical and electronic conductors, wave guides, cavity resonators, superconductor matrixes, vacuum tube and solid-state devices, and glass-to-metal seals.
Copper | 99.99 min |
---|---|
Phosphorus | 0.0003 max |
Remainder Total | 0.004 max |
Tellurium | 0.001 max |
Principal Design Features | Copper, OFE, Oxygen Free Electronic. C26800 has conductivity 101% IACS, the highest among coppers. |
---|---|
Copper Alloys C26800 Applications | Used for electrical and electronic conductors, wave guides, cavity resonators, superconductor matrixes, vacuum tube and solid-state devices, and glass-to-metal seals. |
Copper Alloys C26800 Machinability | The machinability rating of this alloy is 20. (Where Alloy 360 FC Brass is 100). |
Copper Alloys C26800 Forming | This alloy has good ductility and may be readily formed by all conventional methods. Because the alloy is stronger than regular steel it requires more powerful equipment to accomplish forming. Heavy-duty lubricants should be used during cold forming. It is essential to thoroughly clean the part of all traces of lubricant after forming as embrittlement of the alloy may occur at high temperatures if lubricant is left on. |
Copper Alloys C26800 Welding | Soldering is rated as "excellent", brazing is rated as "excellent", oxyacetylene welding is rated as "fair", gas shielded arc welding is rated as "good", coated metal arc welding is "not recommended", spot welding is "not recommended", seam welding is "not recommended" and butt welding is rated as "fair" |
Copper Alloys C26800 Forging | The hot forgeability rating of this alloy is 65. (Forging brass = 100). The recommended hot working temperature for this alloy is between 1400 and 1600 F. |
Copper Alloys C26800 Hot Working | This alloy's capacity for being hot formed is rated as "excellent". |
Copper Alloys C26800 Cold Working | The capacity for cold working this alloy is rated as "excellent". |
Copper Alloys C26800 Annealing | The annealing temperature for this alloy is between 700 and 1200 F. |
Density (lb / cu. in.) | 0.323 |
---|---|
Electrical Resistivity (microhm-cm (at 68 Deg F)) | 10.3 |
Melting Point (Deg F) | 1981 |
Thermal Conductivity | 226 |
Mean Coeff Thermal Expansion | 9.4 |
Modulus of Elasticity Tension | 17000 |
Why Choose Us?
1. who are we?
We are based in Wuxi, China, start from 2007,sell to Domestic Market and Abroad Market. There are total about 51-100 people in our office.
2. how can we guarantee quality?
Always a pre-production sample before mass production; Always final Inspection before shipment;
3.what can you buy from us?
stainless steel plate,stainless steel coil,stainless steel sheet,stainless steel pipe and tube,sainless steel bar
4. why should you buy from us not from other suppliers?
Runs perennial exports of quality assured steel mills ,including Shanxi TISCO, Baosteel, Shanghai Krupp, Ningbo Baoxin, Guangzhou Lianzhong, Zhangjiagang Pohang, Qingdao Pohang, Sweden AvestaPolarit, Finland OUTKUMPU, Spain Acerinox, South Africa Columbus
Contact Us at Any Time